Presentation: SIKA Sikaseal Acrylic Sealant 107 Joint and crack – White – 300ml, designed for sealing joints, repairing and caulking cracks. Can be used indoors and outdoors thanks to its good resistance to bad weather and aging. Advantages: Easy application and smoothing Does not flow Turns into a flexible arced material, even at low temperature Insensitive to weathering after drying The product can be painted but preliminary tests are highly recommended It has good resistance to natural aging Characteristics : Density: 1.65 approx. Application temperature: + 5 ° C to + 40 ° C Polymerisation speed: 1mm approx. in 24 hours at + 23 ° C and 50% RH Skin formation time: approx. (at + 23 ° C and 50% RH) Color: white Packaging: 400ml Reference: 525637 Packaging: 1x SIKA Sikaseal Acrylic Sealant 107 Joint and crack – White – 300ml Delivered in its original packaging Advice: SUPPORT The substrates must be cohesive , healthy, dry and clean. In all cases of use, the supports or the lips of the joints must be rid of all non-adherent parts and any product that may affect the adhesion of the sealant. APPLICATION Respect the DTU 44.1: in particular, do not make joints with a width of less than 5 mm. Placement between the lips of the joint, a Sika JOINTS FUND of a suitable width and the required depth. Apply the putty in a continuous joint avoiding any inclusion of air with a manual, pneumatic or electric gun. Static cracks may be filled with the sealant applied at continuous joint rejection. Tighten and smooth quickly with a spatula before the sealant forms a skin (about 30 minutes at + 23 ° C and 50% RH). The final strength is obtained after complete polymerization. Use Sika products with care. Before use, please consult the manufacturer’s product leaflet available on the sika.fr website.
Product specification :
Density: 1.65 approx .
Application temperature: + 5 ° C to + 40 ° C
Polymerization speed: 1mm approx. in 24 hours at + 23 ° C and 50% RH
Skin formation time: approx. (at + 23 ° C and 50% RH)
- ManoMano ReferenceME8025870